Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
79 kJ/m²
Suspended wall beam without notch impact strength
23°C
ISO 180/1U
68 kJ/m²
flammability
شرایط آزمون
روش آزمون
نتیجه آزمون
UL flame retardant rating
3.2mm
UL 94
HB
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Tensile modulus
23°C
ISO 527-2
12000 Mpa
tensile strength
Break,23°C
ISO 527-2
210 Mpa
Tensile strain
Break,23°C
ISO 527-2
2.5 %
Bending modulus
23°C
ISO 178
10700 Mpa
bending strength
23°C
ISO 178
295 Mpa
Bending strain
ISO 178
3.1 %
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Melting temperature
ISO 11357-3
327 °C
Linear coefficient of thermal expansion
MD:0to100°C
ASTME831
2E-05 cm/cm/°C
Linear coefficient of thermal expansion
MD:100to200°C
ASTME831
1.5E-05 cm/cm/°C
Linear coefficient of thermal expansion
TD:0to100°C
ASTME831
7.6E-05 cm/cm/°C
Linear coefficient of thermal expansion
TD:100to200°C
ASTME831
1.2E-04 cm/cm/°C
Hot deformation temperature
1.8MPa,Unannealed
ISO 75-2/A
>300 °C
Glass transition temperature
DSC
95.0 °C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Shrinkage rate
MD
ASTM D955
0.40 %
Shrinkage rate
TD
ASTM D955
0.80 %
Water absorption rate
24hr
ASTM D570
0.23 %
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Dissipation factor
1MHz
ASTM D150
0.015
Compared to the anti leakage trace index
CTI
UL 746
PLC 0
High voltage arc tracing rate
HVTR
UL 746
mm/min
Volume resistivity
ASTM D257
5.6E+15 ohms·cm
Dielectric strength
3.20mm
ASTM D149
19 KV/mm
Dielectric constant
60Hz
ASTM D150
4.10
Dielectric constant
1MHz
ASTM D150
3.75
Dissipation factor
60Hz
ASTM D150
6E-03
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.