برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap ASTM D256 45 J/m Impact strength of cantilever beam gap ASTM D256 440 J/m Impact strength of cantilever beam gap ASTM D256 450 J/m
flammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating UL 94 HB
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength Yield ASTM D638 49.4 Mpa elongation Break ASTM D638 40 % Bending modulus ASTM D790 2270 Mpa bending strength Yield ASTM D790 79.0 Mpa Friction coefficient Itself - Dynamic ASTM D1894 0.13 Friction coefficient Itself - Static ASTM D1894 0.080 Taber abraser 1000Cycles,1000g,CS-17Wheel ASTM D1044 7.00 mg
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45MPa,Annealed,6.35mm ASTM D648 155 °C Hot deformation temperature 1.8MPa,Annealed,6.35mm ASTM D648 100 °C Linear coefficient of thermal expansion MD:20to80°C ASTM D696 1E-04 cm/cm/°C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون density ASTM D792 1.52 g/cm³ Shrinkage rate MD ASTM D955 1.3-1.6 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Surface resistivity ASTM D257 1E+14 ohms Volume resistivity ASTM D257 1E+16 ohms·cm Dielectric strength ASTM D149 17 KV/mm
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness M-Scale ASTM D785 70
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.