Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus	23°C, 3.20 mm, 注塑	ASTM D638	2650 Mpa
tensile strength	屈服, 23°C, 3.20 mm, 注塑	ASTM D638	59.0 Mpa
elongation	屈服, 23°C, 3.20 mm, 注塑	ASTM D638	> 5.0 %
elongation	elongation	断裂, 23°C, 3.20 mm, 注塑	ASTM D638	> 15 %
Flexural modulus	23°C, 3.20 mm, 注塑	ASTM D790	2850 Mpa
bending strength	23°C, 3.20 mm, 注塑	ASTM D790	96.0 Mpa

injection	شرایط آزمون	روش آزمون	نتیجه آزمون
drying temperature			80 to 90 °C
drying time			2.0 to 4.0 hr
Temperature at the rear of the barrel			190 to 210 °C
Temperature in the middle of the barrel			200 to 220 °C
Temperature at the front of the material cylinder			210 to 230 °C
Spray nozzle temperature			210 to 240 °C
Processing (melt) temperature			210 to 240 °C
Temperature			40 to 70 °C
Back pressure			29.4 to 58.8 Mpa
screw speed			< 80 rpm

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	1.8 MPa, 未退火, 6.40 mm, 注塑，HDT	ASTM D648	87.0 °C
vicat		ASTM D15257	95.0 °C
RTI Elec		UL 746	50.0 °C
RTI Imp		UL 746	50.0 °C
RTI		UL 746	50.0 °C