برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Dart impact 23°C,EnergyatPeakLoad ASTM D3763 4.90 J Impact strength of cantilever beam gap 23°C ISO 180/1A 4.7 kJ/m² Suspended wall beam without notch impact strength 23°C ISO 180/1U 33 kJ/m²
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Tensile modulus ASTM D638 3030 Mpa Tensile modulus ISO 527-2/1 3200 Mpa tensile strength Yield ASTM D638 85.4 Mpa tensile strength Yield ISO 527-2 86.0 Mpa tensile strength Break ASTM D638 83.7 Mpa tensile strength Break ISO 527-2 85.0 Mpa elongation Yield ASTM D638 6.1 % Tensile strain Yield ISO 527-2 6.0 % elongation Break ASTM D638 8.1 % Tensile strain Break ISO 527-2 7.6 % Bending modulus ASTM D790 3450 Mpa Bending modulus ISO 178 3390 Mpa bending strength ASTM D790 149 Mpa bending strength ISO 178 143 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.8MPa,Unannealed,3.20mm ASTM D648 185 °C Hot deformation temperature 1.8MPa,Unannealed,64.0mmSpan ISO 75-2/Af 184 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate MD:24hr ISO 294-4 0.66 % Water absorption rate 24hr,50%RH ASTM D570 0.22 % Shrinkage rate MD:24hr ASTM D955 0.70 % Shrinkage rate TD:24hr ASTM D955 0.70 % Shrinkage rate TD:24hr ISO 294-4 0.70 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.