برگه داده فنی مقایسهflammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 1.5mm UL 94 HB
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Bending modulus ASTM D790 2160 Mpa Tensile strain Break ISO 527-2/50 20 % elongation Break ASTM D638 55 % tensile strength Break ISO 527-2/50 33.0 Mpa tensile strength Yield ISO 527-2/50 46.0 Mpa tensile strength Yield ASTM D638 43.0 Mpa bending strength ISO 178 67.0 Mpa bending strength ASTM D790 63.3 Mpa Bending modulus ISO 178 2200 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature Unannealed ASTM D648 85 °C Hot deformation temperature Annealed ASTM D648 95 °C Linear coefficient of thermal expansion MD ISO 11359-2 9E-05 cm/cm/°C Vicat softening temperature -- ISO 306/B50 94.0 °C Vicat softening temperature -- ISO 306/A50 105 °C Vicat softening temperature ASTM D15256 105 °C Hot deformation temperature 1.8MPa,Annealed ISO 75-2/A 97.0 °C Hot deformation temperature 1.8MPa,Unannealed ISO 75-2/A 80.0 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate ISO 294-4 0.40-0.70 % Melt Volume Flow Rate (MVR) 220°C/10.0kg ISO 1133 23.0 cm3/10min melt mass-flow rate 220°C/10.0kg ASTM D1238 23 g/10min
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness R-Scale ASTM D785 105
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.