برگه داده فنی مقایسهflammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 1.5 mm UL 94 HB
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength 23°C ASTM D638 59.0 Mpa Bending modulus 23°C ASTM D790 2350 Mpa bending strength 23°C ASTM D790 94.0 Mpa
injection شرایط آزمون روش آزمون نتیجه آزمون drying temperature 100 to 110 °C drying time 3.0 to 4.0 hr Suggested maximum moisture content 0.020 % Hopper temperature 60 to 80 °C Temperature at the rear of the barrel 220 to 250 °C Temperature in the middle of the barrel 240 to 270 °C Temperature at the front of the material cylinder 240 to 270 °C Spray nozzle temperature 230 to 270 °C Processing (melt) temperature 250 to 270 °C Mold temperature 70 to 90 °C Back pressure 0.345 to 0.689 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.8 MPa, Unannealed, 6.35 mm ASTM D648 112 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 240°C/5.0 kg ASTM D1238 7.5 g/10 min Shrinkage rate Flow : 3.20 mm ASTM D955 0.40 - 0.60 % Shrinkage rate 3.20 mm ISO 2577 0.40 - 0.60 %
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness R-Scale, 23°C ASTM D785 116 Rockwell hardness R -Sale, 23°C ISO 2039-2 116