Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
41 kJ/m²
Suspended wall beam without notch impact strength
23°C
ASTM D4812
620 J/m
flammability
شرایط آزمون
روش آزمون
نتیجه آزمون
UL flame retardant rating
1.00mm
UL 94
V-0
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
--1
ASTM D638
12000 Mpa
crack
ASTM D638
141 Mpa
crack
ISO 527-2/5
140 Mpa
crack
ASTM D638
2.3 %
crack
ISO 527-2/5
2.2 %
50.0mm span
ASTM D790
11700 Mpa
--5
ISO 178
10100 Mpa
--6
ISO 178
189 Mpa
Fracture, 50.0mm span
ASTM D790
211 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
1.8MPa,Unannealed,3.20mm
ASTM D648
98.0 °C
Linear coefficient of thermal expansion
MD:23to80°C
ISO 11359-2
1.6E-05 cm/cm/°C
Linear coefficient of thermal expansion
TD:23to80°C
ISO 11359-2
5.8E-05 cm/cm/°C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
melt mass-flow rate
300°C/1.2kg
ASTM D1238
17 g/10min
melt mass-flow rate
300°C/2.16kg
ASTM D1238
39 g/10min
Melt Volume Flow Rate (MVR)
300°C/1.2kg
ISO 1133
12.0 cm3/10min
Melt Volume Flow Rate (MVR)
300°C/2.16kg
ISO 1133
30.0 cm3/10min
Shrinkage rate
MD:24hr
ASTM D955
0.10-0.25 %
Shrinkage rate
TD:24hr
ASTM D955
0.10-0.25 %