برگه داده فنی مقایسهoptical performance شرایط آزمون روش آزمون نتیجه آزمون Refractive index ASTM D542/ISO 489 1.49 Transmittance rate ASTM D1003/ISO 13468 91 %
other شرایط آزمون روش آزمون نتیجه آزمون characteristic 抗冲击
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Elongation at Break ASTM D638/ISO 527 380 % bending strength ASTM D790/ISO 178 720 kg/cm²(MPa)[Lb/in²] Bending modulus ASTM D790/ISO 178 19000 kg/cm²(MPa)[Lb/in²] Rockwell hardness ASTM D785 45 elongation ASTM D638/ISO 527 5.9 % tensile strength ASTM D638/ISO 527 390 kg/cm²(MPa)[Lb/in²] Tensile modulus ASTM D638/ISO 527 600 kg/cm²(MPa)[Lb/in²] Elongation at Break ASTM D638/ISO 527 720 % Impact strength of cantilever beam gap ASTM D256/ISO 179 5.9 kg·cm/cm(J/M)ft·lb/in Impact strength of cantilever beam gap ASTM D256/ISO 179 6 kg·cm/cm(J/M)ft·lb/in Impact strength of cantilever beam gap ASTM D256/ISO 179 7 kg·cm/cm(J/M)ft·lb/in Impact strength of cantilever beam gap ASTM D256/ISO 179 57.9 kg·cm/cm(J/M)ft·lb/in
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Vicat softening temperature ASTM D1525/ISO R306 98 ℃(℉) Hot deformation temperature HDT ASTM D648/ISO 75 79 ℃(℉)
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Water absorption rate ASTM D570/ISO 62 0.4 % melt mass-flow rate ASTM D1238/ISO 1133 1.0 g/10min Shrinkage rate ASTM D955 0.3-0.8 % density ASTM D792/ISO 1183 1.19
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.