Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	屈服, 23°C, 3.20 mm, 注塑	ASTM D638	98.1 Mpa
elongation	断裂, 23°C, 3.20 mm, 注塑	ASTM D638	3.0 %
Flexural modulus	23°C, 3.20 mm, 注塑	ASTM D790	4900 Mpa
bending strength	23°C, 3.20 mm, 注塑	ASTM D790	142 Mpa

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Volume resistivity	23°C	ASTM D257	1.0E+14 ohms·cm
dielectric strength	23°C, 1.00 mm	ASTM D149	22 KV/mm
dielectric constant	23°C, 1 MHz	ASTM D150	3.00
Compared to the Leakage Tracking Index (CTI)	解决方案 A	IEC 60112	PLC 2

injection	شرایط آزمون	روش آزمون	نتیجه آزمون
drying temperature			80 to 100 °C
drying time			4.0 to 5.0 hr
Suggested maximum moisture content			0.10 %
Temperature at the rear of the barrel			265 to 275 °C
Temperature in the middle of the barrel			270 to 280 °C
Temperature at the front of the material cylinder			270 to 285 °C
Spray nozzle temperature			270 to 280 °C
Processing (melt) temperature			270 to 290 °C
Temperature			80 to 110 °C
Back pressure			0.981 to 2.94 Mpa
screw speed			60 to 150 rpm

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	1.8 MPa, 未退火, 6.40 mm, 注塑，HDT	ASTM D648	230 °C
melting temperature		ASTM D3418	260 °C
Linear coefficient of thermal expansion	流动	ASTM D696	3.0E-5 cm/cm/°C