برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap 23°C,3.20mm ASTM D256 180 J/m Impact strength of cantilever beam gap 23°C,6.40mm ASTM D256 170 J/m Impact strength of cantilever beam gap -30°C,3.20mm ASTM D256 78 J/m Impact strength of cantilever beam gap -30°C,6.40mm ASTM D256 69 J/m
flammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating UL 94 HB
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength Yield,3.20mm ASTM D638 49.0 Mpa elongation Break,3.20mm ASTM D638 20 % Bending modulus 3.20mm ASTM D790 2550 Mpa bending strength Yield,3.20mm ASTM D790 78.5 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45MPa,Unannealed,6.40mm ASTM D648 115 °C Hot deformation temperature 1.8MPa,Unannealed,6.40mm ASTM D648 106 °C Vicat softening temperature ASTM D15255 116 °C RTI Elec UL 746 60.0 °C RTI Imp UL 746 60.0 °C RTI UL 746 60.0 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون density ASTM D792 1.06 g/cm³ melt mass-flow rate 220°C/10.0kg ASTM D1238 3.0 g/10min Shrinkage rate MD:3.20mm ASTM D955 0.40-0.70 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون 1.00mm 1.00mm ASTM D149 33 KV/mm Arc resistance ASTM D495 PLC6 Compared to the anti leakage trace index CTI)6 UL 746 PLC 0
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness R-Scale ASTM D785 111