برگه داده فنی مقایسهflammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating UL 94 V-0
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength ASTM D638/ISO 527 86 kg/cm²(MPa)[Lb/in²] Bending modulus ASTM D790/ISO 178 6130 kg/cm²(MPa)[Lb/in²] bending strength ASTM D790/ISO 178 128 kg/cm²(MPa)[Lb/in²] Elongation at Break ASTM D638/ISO 527 2.8 % tensile strength ISO 527-2 86.0 Mpa Tensile strain Break ISO 527-2 2.8 % Bending modulus ISO 178 6130 Mpa bending strength ISO 178 128 Mpa tensile strength ISO 527-1/-2 86 Mpa bending strength ISO 178 128 Mpa Bending modulus ISO 178 6130 Mpa Charpy Notched Impact Strength ISO 179/1eA 3.9 KJ/m
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Combustibility (rate) UL 94 V-0 Hot deformation temperature 1.8MPa,Unannealed ISO 75-2/A 205 °C Linear coefficient of thermal expansion MD:23to55°C Internal Method 5E-05 cm/cm/°C Linear coefficient of thermal expansion TD:23to55°C Internal Method 7E-05 cm/cm/°C Hot deformation temperature 1.8Mpa ISO 75-1/-2 205 °C UL flame retardant rating UL 94 V-0
Physical properties شرایط آزمون روش آزمون نتیجه آزمون density ASTM D792/ISO 1183 1.56 Water absorption rate 23°C,24hr ISO 62 0.10 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Dielectric strength 3.00mm IEC 60243-1 24 KV/mm
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness M-Scale ISO 2039-2 85
Supplementary Information شرایط آزمون روش آزمون نتیجه آزمون ColourNumber EF2001/ED3002