Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
38 kJ/m²
Suspended wall beam without notch impact strength
23°C
ASTM D4812
520 J/m
flammability
شرایط آزمون
روش آزمون
نتیجه آزمون
UL flame retardant rating
1.00mm
UL 94
V-0
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
--1
ASTM D638
15300 Mpa
crack
ASTM D638
154 Mpa
crack
ISO 527-2/5
153 Mpa
crack
ASTM D638
2.1 %
crack
ISO 527-2/5
1.9 %
Bending modulus
50.0mmSpan
ASTM D790
14900 Mpa
bending strength
Break,50.0mmSpan
ASTM D790
223 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
1.8MPa,Unannealed,3.20mm
ASTM D648
107 °C
Linear coefficient of thermal expansion
MD:-40to40°C
ASTME831
1.4E-05 cm/cm/°C
Linear coefficient of thermal expansion
TD:-40to40°C
ASTME831
5.1E-05 cm/cm/°C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
melt mass-flow rate
300°C/2.16kg
ASTM D1238
13 g/10min
melt mass-flow rate
300°C/5.0kg
ASTM D1238
49 g/10min
Melt Volume Flow Rate (MVR)
300°C/5.0kg
ASTM D1238
29.5 cm3/10min
Shrinkage rate
MD:24hr
ASTM D955
0.050-0.20 %
Shrinkage rate
TD:24hr
ASTM D955
0.050-0.20 %