برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون elongation Break ASTM D-638 40 % Impact strength of cantilever beam gap ASTM D-256 4 kg.cm/cm tensile strength Yield ASTM D-638 25 Mpa Bending modulus ASTM D-790 24000 kg/cm tensile strength Yield ASTM D-638 250 kg/cm bending strength ASTM D-790 5300 psi Impact strength of cantilever beam gap ASTM D-256 0.7 ft.lb/in bending strength ASTM D-790 370 kg/cm tensile strength Yield ASTM D-638 3600 psi bending strength ASTM D-790 36 Mpa Bending modulus ASTM D-790 340 psi Bending modulus ASTM 790 2350 Mpa Impact strength of cantilever beam gap ASTM D-256 40 J/m
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45Mpa ASTM D-648 265 °F Flame resistance ASTM UL94 V-0 CLASS Hot deformation temperature 0.45Mpa ASTM D-648 130 °C Hot deformation temperature 1.82Mpa ASTM D-648 165 °F Hot deformation temperature 1.82Mpa ASTM D-648 75 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون density ASTM D-792 0.9-1.3
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.