برگه داده فنی مقایسهelastomer شرایط آزمون روش آزمون نتیجه آزمون Permanent compression deformation 23℃, 22.0 hr ASTM D395 18 % Permanent compression deformation 70℃, 22.0 hr ASTM D395 36 % Permanent compression deformation 100℃, 22.0 hr ASTM D395 53 % tensile strength 100%Strain ASTM D412 1.80 Mpa tensile strength 300%Strain ASTM D412 3.10 Mpa tensile strength Break ASTM D412 5.00 Mpa elongation Break ASTM D412 600 % tear strength ASTM D624 24.0 kN/m tensile strength 100%Strain ASTM D412 1.80 Mpa tensile strength 300%Strain ASTM D412 3.10 Mpa tensile strength Break ASTM D412 5.00 Mpa elongation Break ASTM D412 600 % tear strength ASTM D624 24.0 kN/m Permanent compression deformation 23°C,22hr ASTM D395 18 % Permanent compression deformation 70°C,22hr ASTM D395 36 % Permanent compression deformation 100°C,22hr ASTM D395 53 %
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate MD ASTM D955 2.8 % Shrinkage rate TD ASTM D955 1.5 % Shore hardness Shore A ASTM D412 60 Shrinkage rate MD ASTM D955 2.8 % Shrinkage rate TD ASTM D955 1.5 %
hardness شرایط آزمون روش آزمون نتیجه آزمون Shore hardness ShoreA ASTM D2240 60
Supplementary Information شرایط آزمون روش آزمون نتیجه آزمون ozone resistance Stressed ASTM D518 NoCracks
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.