برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap ASTM D-256 2.5 kg.cm/cm tensile strength Yield ASTM D-638 340 kg/cm tensile strength Yield ASTM D-638 4800 psi Bending modulus ASTM 790 4510 Mpa tensile strength ASTM D-638 33 Mpa bending strength ASTM D-790 570 kg/cm bending strength ASTM D-790 8100 psi Bending modulus ASTM D-790 650 psi bending strength ASTM D-790 56 Mpa Impact strength of cantilever beam gap ASTM D-256 25 J/m Impact strength of cantilever beam gap ASTM D-256 0.5 ft.lb/in elongation Break ASTM D-638 11 % Bending modulus ASTM D-790 46000 kg/cm
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.82Mpa ASTM D-648 230 °F Hot deformation temperature 0.45Mpa ASTM D-648 300 °F Hot deformation temperature 0.45Mpa ASTM D-648 150 °C Flame resistance ASTM UL94 HB CLASS Hot deformation temperature 1.82Mpa ASTM D-648 110 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate ASTM D-955 0.6-1.0 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.