Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
150 kJ/m²
Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
NoBreak
flammability
شرایط آزمون
روش آزمون
نتیجه آزمون
Burning rate
1.00mm
ISO 3795
<100 mm/min
FMVSS flammability
FMVSS302
B
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Tensile modulus
ISO 527-2
2100 Mpa
tensile strength
Yield
ISO 527-2
55.0 Mpa
Tensile strain
Yield
ISO 527-2
20 %
Nominal tensile fracture strain
ISO 527-2
25 %
Bending modulus
ISO 178
2000 Mpa
bending strength
3.5%Strain
ISO 178
55.0 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
AnnealingTemperature
160 °C
AnnealingTime-Optional
30.0 min/mm
Hot deformation temperature
0.45MPa,Unannealed
ISO 75-2/B
136 °C
Hot deformation temperature
1.8MPa,Unannealed
ISO 75-2/A
78.0 °C
Linear coefficient of thermal expansion
MD
ISO 11359-2
1.1E-04 cm/cm/°C
Linear coefficient of thermal expansion
TD
ISO 11359-2
1.2E-04 cm/cm/°C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
MediumDensity
1.15 g/cm³
melt mass-flow rate
ISO 1133
6.0 g/10min
Melt Volume Flow Rate (MVR)
190°C/2.16kg
ISO 1133
4.30 cm3/10min
hardness
شرایط آزمون
روش آزمون
نتیجه آزمون
Rockwell hardness
M-Sale
ISO 2039-2
69
Rockwell hardness
R-Sale
ISO 2039-2
116
Supplementary Information
شرایط آزمون
روش آزمون
نتیجه آزمون
Emission
VDA275
<2.00 mg/kg