برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Dart impact 23°C,EnergyatPeakLoad ASTM D3763 75.0 J
flammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 1.5mm UL 94 V-0
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Tensile modulus ASTM D638 2320 Mpa tensile strength Yield ASTM D638 64.0 Mpa tensile strength Break ASTM D638 62.0 Mpa elongation Yield ASTM D638 6.0 % elongation Break ASTM D638 110 % Bending modulus 50.0mmSpan ASTM D790 2330 Mpa bending strength Yield,50.0mmSpan ASTM D790 101 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45MPa,Unannealed,3.20mm ASTM D648 142 °C Hot deformation temperature 1.8MPa,Unannealed,3.20mm ASTM D648 138 °C Vicat softening temperature ISO 306/B120 146 °C Linear coefficient of thermal expansion MD:-40to95°C ASTME831 6.8E-05 cm/cm/°C Linear coefficient of thermal expansion TD:-40to95°C ASTME831 6.8E-05 cm/cm/°C RTI Elec UL 746 125 °C RTI Imp UL 746 115 °C RTI Str UL 746 125 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 300°C/1.2kg ASTM D1238 6.3 g/10min Shrinkage rate MD2 Internal Method 0.60-0.80 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Compared to the anti leakage trace index CTI UL 746 PLC 3 High arc combustion index HAI UL 746 PLC 1 Hot wire ignition HWI UL 746 PLC 3