برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap 23℃,6.4mm ASTM D256 15 kJ/m² Impact strength of cantilever beam gap -30℃,6.4mm ASTM D256 15 kJ/m² Impact strength of cantilever beam gap 23℃,3.2mm ASTM D256 14 kJ/m² Impact strength of cantilever beam gap -30℃,3.2mm ASTM D256 14 kJ/m²
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength Yield 50mm/min,3.2mm ASTM D638 430 kg/cm2 elongation Break50mm/min,3.2mm ASTM D638 32 % bending strength 10mm/min,6.4mm ASTM D790 575 kg/cm2 Bending modulus 10mm/min,6.4mm ASTM D790 21300 kg/cm2 Rockwell hardness ASTM D785 110
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature Unannealed18.6kg,6.4mm ASTM D648 82 °C Hot deformation temperature Unannealed4.6kg,6.4mm ASTM D648 86 °C Vicat softening temperature 5kg,50℃/h ASTM D1525 97 °C flammability UL 94 HB Relative Heat Index (RTI) 电气 UL -746B 60 °C Relative Heat Index (RTI) 有机械冲击 UL -746B 60 °C Relative Heat Index (RTI) 无机械冲击 UL -746B 60 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون density ASTM D792 1.05 Shrinkage rate Flow,3.2mm ASTM D955 0.4-0.7 % melt mass-flow rate 220℃,10kg ASTM D1238 25 g/10min
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Compared to the anti leakage trace index IEC 60112 V Arc resistance 23℃ ASTM D495 6 ohm.cm