برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength - ASTM D638 560 kg/cm2 Rockwell hardness ASTM D785 110 R Impact strength of cantilever beam gap - ASTM D256 12.0 ft.ib/in bending strength - ASTM D790 11200 psi bending strength - ASTM D790 77 Mpa bending strength - ASTM D790 790 kg/cm2 elongation Break ASTM D638 >100 % tensile strength - ASTM D638 7960 psi tensile strength - ASTM D638 55 Mpa Impact strength of cantilever beam gap - ASTM D256 635 J/m Impact strength of cantilever beam gap - ASTM D256 65 kg.cm/cm Bending modulus - ASTM D790 320 psi Bending modulus - ASTM D790 2205 Mpa Bending modulus - ASTM D790 22500 kg/cm2
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.82MPa ASTM D648 225 ℉ Hot deformation temperature 1.82MPa ASTM D648 108 °C melt mass-flow rate 4 g/10min
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate ASTM D955 0.5-0.8 % density ASTM D792 1.13
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.