Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
60 kJ/m²
Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
62 kJ/m²
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
tensile strength
Break,23°C
ASTM D638
117 Mpa
tensile strength
Break,93°C
ASTM D638
72.4 Mpa
tensile strength
Break
ISO 527-2/1A/5
130 Mpa
tensile strength
80°C
ISO 527-2/1A
75.0 Mpa
elongation
Break,-40°C
ASTM D638
1.8 %
elongation
Break,23°C
ASTM D638
1.9 %
elongation
Break,93°C
ASTM D638
2.4 %
Tensile strain
Break
ISO 527-2/1A/5
2.0 %
Tensile strain
Break,80°C
ISO 527-2/1A
2.3 %
Bending modulus
23°C
ISO 178
9000 Mpa
Bending modulus
80°C
ISO 178
6400 Mpa
bending strength
23°C
ISO 178
180 Mpa
Tensile modulus
-40°C
ASTM D638
11700 Mpa
Tensile modulus
23°C
ASTM D638
9170 Mpa
Tensile modulus
93°C
ASTM D638
5690 Mpa
Tensile modulus
--
ISO 527-2/1A/1
9200 Mpa
Tensile modulus
80°C
ISO 527-2/1A
6200 Mpa
tensile strength
Break,-40°C
ASTM D638
176 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
1.8MPa,Unannealed
ASTM D648
152 °C
Hot deformation temperature
1.8MPa,Unannealed
ISO 75-2/A
152 °C