برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength Yield ASTM D-638 28 Mpa Impact strength of cantilever beam gap ASTM D-256 1.7 ft.lb/in tensile strength Yield ASTM D-638 4100 psi tensile strength Yield ASTM D-638 290 kg/cm Impact strength of cantilever beam gap ASTM D-256 90 J/m bending strength ASTM D-790 35 Mpa elongation Break ASTM D-638 60 % bending strength ASTM D-790 360 kg/cm Bending modulus ASTM D-790 230 psi bending strength ASTM D-790 5100 psi Bending modulus ASTM D-790 16000 kg/cm Impact strength of cantilever beam gap ASTM D-256 9 kg.cm/cm Bending modulus ASTM 790 1570 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.82Mpa ASTM D-648 75 °C Hot deformation temperature 0.45Mpa ASTM D-648 135 °C Hot deformation temperature 0.45Mpa ASTM D-648 275 °F Hot deformation temperature 1.82Mpa ASTM D-648 165 °F Flame resistance ASTM D-UL94 HB
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate ASTM D-955 0.9-1.4 % density ASTM D-792 0.96
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.