Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
30 kJ/m²
Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
35 kJ/m²
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Tensile modulus
ISO 527-2
9000 Mpa
tensile strength
Break
ISO 527-2
120 Mpa
Tensile strain
Break
ISO 527-2
2.5 %
Bending modulus
ISO 178
7700 Mpa
bending strength
ISO 178
165 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
0.45MPa,Unannealed
ISO 75-2/B
215 °C
Hot deformation temperature
1.8MPa,Unannealed
ISO 75-2/A
205 °C
Melting temperature
ISO 11357-3
220 °C
Linear coefficient of thermal expansion
MD
ISO 11359-2
3.5E-05 cm/cm/°C
Linear coefficient of thermal expansion
TD
ISO 11359-2
5E-05 cm/cm/°C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Shrinkage rate
MD
ISO 294-4
0.30 %
Water absorption rate
Saturation,23°C
ISO 62
5.5 %
Water absorption rate
Equilibrium,23°C,50%RH
ISO 62
1.7 %
Shrinkage rate
TD
ISO 294-4
0.90 %
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Relative permittivity
100Hz
IEC 60250
3.50
Relative permittivity
1MHz
IEC 60250
3.30
Dissipation factor
100Hz
IEC 60250
5E-03
Dissipation factor
1MHz
IEC 60250
0.014
Surface resistivity
IEC 60093
-- ohms
Volume resistivity
IEC 60093
1E+14 ohms·cm
Dielectric strength
IEC 60243-1
35 KV/mm