Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
16 kJ/m²
Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
NoBreak
flammability
شرایط آزمون
روش آزمون
نتیجه آزمون
UL flame retardant rating
1.6mm
UL 94
HB
Extreme Oxygen Index
ISO 4589-2
25 %
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Tensile strain
Yield,23°C
ISO 527-2
20 %
elongation
Break,23°C
ASTM D638
80 %
Bending modulus
23°C
ASTM D790
1800 Mpa
Bending modulus
23°C
ISO 178
1800 Mpa
bending strength
23°C
ASTM D790
70.0 Mpa
bending strength
23°C
ISO 178
70.0 Mpa
Tensile modulus
23°C
ISO 527-2/1A
1900 Mpa
tensile strength
Yield,23°C
ASTM D638
50.0 Mpa
tensile strength
Yield,23°C
ISO 527-2/1A
47.0 Mpa
tensile strength
Break,23°C
ISO 527-2/1A
44.0 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
0.45MPa,Unannealed
ASTM D648
200 °C
Hot deformation temperature
1.8MPa,Unannealed
ASTM D648
63.0 °C
Hot deformation temperature
1.8MPa,Unannealed
ISO 75-2/Af
65.0 °C
Melting temperature
ISO 11357-3
263 °C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Water absorption rate
23°C,24hr
ISO 62
1.1 %
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Dissipation factor
IEC 60250
0.020
Compared to the anti leakage trace index
SolutionA
IEC 60112
PLC 1
Compared to the anti leakage trace index
SolutionB
IEC 60112
PLC 1
Surface resistivity
IEC 60093
1E+15 ohms
Volume resistivity
IEC 60093
1E+15 ohms·cm
Dielectric strength
2.00mm
IEC 60243-1
30 KV/mm
Relative permittivity
IEC 60250
3.20