Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus	100%	DIN 53504-S2	10 N/mm
Impact strength of cantilever beam gap	＋23℃	DIN 53453	不破裂 KJ/m
Shore hardness		DIN 53505	96 shoreA
tensile strength		DIN 53504-S2	55 N/mm
compression set	室温	DIN 53517	30 %
Impact strength of cantilever beam gap	－30℃	DIN 53453	不破裂 KJ/m
tensile strength	80℃水中21天	DIN 53504-S2	37 N/mm
Tensile modulus	300%	DIN 53504-S2	18 N/mm
Friction loss		DIN 53516	25 mm
elongation at break	80℃水中21天	DIN 53504-S2	500 %
elongation at break	elongation at break		DIN 53504-S2	500 %
Tensile modulus	20%	DIN 53504-S2	6 N/mm
tear strength		DIN 53515	100 N/mm
Shore hardness		DIN 53505	48 Shore D
compression set	70℃	DIN 53517	45 %
Tensile modulus	100%	ASTM D412/ISO 527	6 Mpa/Psi
Tensile modulus	Tensile modulus	300%	ASTM D412/ISO 527	10 Mpa/Psi
tensile strength		ASTM D412/ISO 527	55 Mpa/Psi
tear strength		ASTM D624/ISO 34	100 n/mm²
Shore hardness		ASTM D2240/ISO 868	96 Shore A
Shore hardness	Shore hardness		ASTM D2240/ISO 868	48 Shore D