برگه داده فنی مقایسهmachinability شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate TD ASTM D-955 6.0 Shrinkage rate MD ASTM D-955 2.0
Basic Performance شرایط آزمون روش آزمون نتیجه آزمون Water absorption rate 23℃水中24h ASTM D-570 0.13 %
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Bending modulus ISO 178 (ASTM D-790) 5880(60000) MPa(KG/cm Rockwell hardness ISO 2039-2 (ASTM D-785) M91 Impact strength of cantilever beam gap 4mm with notch 3.2mm with notch ISO 180 (ASTM D-256) 13(14) KJ/m bending strength ISO 178 (ASTM D-790) 140(1400) Mpa tensile strength Break ISO R-527 (ASTM D-638) 100(1000) MPa(KG/cm Tensile modulus ISO R-527 (ASTM D-638) 5700(58000) MPa(KG/cm Elongation at Break ISO R-527 (ASTM D-638) 4 %
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Vicat softening temperature ISO 306 150 °C Linear coefficient of thermal expansion ASTM D-696 2.5 Combustibility 1.47mm厚 UL 94 V-2 Hot deformation temperature 1.80MPa,18.6kg/cm ISO 75(ASTM D-648) 139 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Spiral flow length 3mm厚 出光法 0.13 CM
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Induced positive connection 10 ASTM D-150 9×10 Arc resistance ASTM D-495 110 sec Dielectric constant 10 ASTM D-150 3.15 Dielectric strength 1.6mm厚 ASTM D-149 <22 KV/mm Induced positive connection 60Hz ASTM D-150 8×10 Inherent resistance of volume ASTM D-257 <10 Ω·cm Dielectric constant 60Hz ASTM D-150 3.25