thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat Deflection Temperature	1.8MPa,未退火，HDT	ISO 75-2/A	102 °C
vicat		ISO 306/B50	122 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	7E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	7E-05 cm/cm/°C

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
bending strength		ISO 178	80.0 Mpa
Tensile modulus		ISO 527-2	2200 Mpa
tensile strength	屈服	ISO 527-2	50.0 Mpa
Tensile strain	屈服	ISO 527-2	4.0 %
Nominal tensile fracture strain		ISO 527-2	>50 %
flexural modulus		ISO 178	2250 Mpa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak
Multi axis Instrumented Impact Energy	-20°C2	内部方法	4.00 J
	Multi axis Instrumented Impact Energy	23°C	ISO 6603-2	35.0 J
	Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	23°C2	内部方法	10.0 J

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Surface Resistivity		IEC 60093	>1.0E+15 ohms
volume resistivity		IEC 60093	>1.0E+15 ohms·cm
dielectric constant	1.00GHz	IEC 60250	2.80
Dissipation Factor	1.00GHz	IEC 60250	5E-03

Physical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Melt volume flow rate	260°C/5.0kg	ISO 1133	14.0 cm3/10min
shrinkage rate	MD	ISO 294-4	0.60 %
Water absorption rate	饱和,23°C	ISO 62	0.60 %