برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap 23°C,6.35mm ASTM D256 220 J/m Impact strength of cantilever beam gap 23°C,3.18mm ASTM D256 250 J/m
flammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 1.6mm UL 94 HB
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون bending strength Yield,23°C ASTM D790 68.9 Mpa Bending modulus 23°C ASTM D790 2340 Mpa elongation Break,23°C,3.18mm ASTM D638 30 % tensile strength Break,23°C,3.18mm ASTM D638 34.5 Mpa tensile strength Yield,23°C,3.18mm ASTM D638 39.3 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون RTI Str 1.6mm UL 746 60.0 °C RTI Imp 1.6mm UL 746 60.0 °C RTI Elec 1.6mm UL 746 60.0 °C Vicat softening temperature ASTM D15254 100 °C Hot deformation temperature 1.8MPa,Unannealed,12.7mm ASTM D648 82.0 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Water absorption rate 24hr ASTM D570 <0.30 % Shrinkage rate MD ASTM D955 <0.40 % melt mass-flow rate 220°C/10.0kg ASTM D1238 18 g/10min melt mass-flow rate 200°C/5.0kg ASTM D1238 1.8 g/10min density ASTM D792 1.03 g/cm³
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Hot wire ignition 1.57mm UL 746 PLC 3 sec High voltage arc tracing rate 1.57mm UL 746 mm/min High arc combustion index 1.57mm UL 746 PLC 0
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness R-Sale,23°C ASTM D785 110