Impact strength of simply supported beam without notch
-30°C
ISO 179
NoBreak
Impact strength of simply supported beam without notch
23°C
ISO 179
NoBreak
flammability
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot filament ignition temperature
0.71mm
IEC 60695-2-13
960 °C
Hot filament ignition temperature
1.5mm
IEC 60695-2-13
960 °C
Hot filament ignition temperature
3.0mm
IEC 60695-2-13
750 °C
UL flame retardant rating
0.40mm
UL 94
V-2
Burning wire flammability index
0.71mm
IEC 60695-2-12
960 °C
Burning wire flammability index
1.5mm
IEC 60695-2-12
960 °C
Burning wire flammability index
3.0mm
IEC 60695-2-12
960 °C
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Tensile modulus
ISO 527-2/1
3000 Mpa
tensile strength
Yield
ISO 527-2/50
84.0 Mpa
Tensile strain
Yield
ISO 527-2
4.4 %
Tensile strain
Break
ISO 527-2
30 %
Bending modulus
ISO 178
2900 Mpa
bending strength
ISO 178
94.0 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Melting temperature
ISO 11357-3
260 °C
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Shrinkage rate
TD:2.00mm
ISO 294-4
2.1 %
Shrinkage rate
MD:2.00mm
ISO 294-4
2.1 %
Water absorption rate
23°C,24hr
ISO 62
1.7 %
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Volume resistivity
2.00mm
IEC 60093
10 ohms·cm
Dielectric strength
1.00mm
IEC 60243-1
18 KV/mm
Compared to the anti leakage trace index
3.00mm
IEC 60112
V