Impact strength of simply supported beam without notch
-30℃-30°C
ISO 179/1eU
90 kJ/m²
Impact strength of simply supported beam without notch
23℃23°C
ISO 179/1eU
90 kJ/m²
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Tensile modulus
ISO 527-2
6500 Mpa
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
1.8 MPa,Unannealed264 psi, Unannealed
ISO 75-2/A
160 °C
Hot deformation temperature
8.0 MPa,Unannealed1160 psi, Unannealed
ISO 75-2/C
90 °C
Melting temperature
ISO 11357-3
178 °C
Linear coefficient of thermal expansion
MDFlow
ISO 11359-2
0.000020 1/℃
Linear coefficient of thermal expansion
TDTransverse
ISO 11359-2
0.00015 1/℃
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
density
ISO 1183
1.22 g/cm³
Shrinkage rate
TDAcross Flow
ISO 294-4
0.8 %
Shrinkage rate
MDFlow
ISO 294-4
0.1 %
Water absorption rate
Saturation,23℃Saturation, 73°F
ISO 62
1.1 %
Water absorption rate
Equilibrium,23℃,50% RHEquilibrium, 73°F, 50% RH
ISO 62
0.6 %
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Surface Resistance
IEC 60093
-- ohms
Volume resistivity
IEC 60093
-- ohms·cm
Dielectric strength
IEC 60243-1
-- KV/mm
Compared to the leakage tracking index, the comparative tracking index
IEC 60112
-- V
flame retardant performance
شرایط آزمون
روش آزمون
نتیجه آزمون
UL flame retardant rating
UL 94
HB