Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus	23°C, 3.20 mm, 注塑	ASTM D638	2050 Mpa
tensile strength	屈服, 23°C, 3.20 mm, 注塑	ASTM D638	48.0 Mpa
elongation	屈服, 23°C, 3.20 mm, 注塑	ASTM D638	> 5.0 %
elongation	elongation	断裂, 23°C, 3.20 mm, 注塑	ASTM D638	15 %
Flexural modulus	23°C, 3.20 mm, 注塑	ASTM D790	2250 Mpa
bending strength	23°C, 3.20 mm, 注塑	ASTM D790	71.0 Mpa

injection	شرایط آزمون	روش آزمون	نتیجه آزمون
drying temperature			80 to 90 °C
drying time			2.0 to 4.0 hr
Temperature at the rear of the barrel			180 to 200 °C
Temperature in the middle of the barrel			190 to 210 °C
Temperature at the front of the material cylinder			200 to 220 °C
Spray nozzle temperature			190 to 220 °C
Processing (melt) temperature			190 to 220 °C
Temperature			40 to 60 °C
Back pressure			29.4 to 58.8 Mpa
screw speed			30 to 60 rpm

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	1.8 MPa, 未退火, 6.40 mm, 注塑，HDT	ASTM D648	81.0 °C
vicat		ASTM D15257	89.0 °C
RTI Elec		UL 746	50.0 °C
RTI Imp		UL 746	50.0 °C
RTI		UL 746	50.0 °C