برگه داده فنی مقایسهflammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating UL 94 HB
elastomer شرایط آزمون روش آزمون نتیجه آزمون tensile strength 50%Strain ASTM D412 14.7 Mpa tear strength ASTM D624 172 kN/m Permanent compression deformation ASTM D395 57 %
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength Yield ASTM D638 31.0 Mpa elongation Break ASTM D638 700 % Bending modulus ASTM D790 162 Mpa Compressive modulus ASTM D695 13.3 Mpa Taber abraser 1000Cycles ASTM D1044 13.0 mg
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.8MPa,Unannealed ASTM D648 101 °C Brittle temperature ASTM D746 -65.0 °C Vicat softening temperature ASTM D1525 180 °C Melting temperature DSC 203 °C Linear coefficient of thermal expansion MD ASTM D696 1.4E-04 cm/cm/°C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 230°C/2.16kg ASTM D1238 20 g/10min Shrinkage rate MD:2.00mm ASTM D955 1.1 % Water absorption rate Equilibrium,23°C,65%RH ASTM D570 0.40 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Volume resistivity ASTM D257 6E+13 ohms·cm Dielectric strength ASTM D149 30 KV/mm
hardness شرایط آزمون روش آزمون نتیجه آزمون Shore hardness ShoreD ASTM D2240 52