برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength Yield23℃ ASTM D638 60 Mpa tensile strength 23℃ 50mm/min ASTM D638 46 Mpa elongation Yield23℃ 50mm/min ASTM D638 4 % elongation 23℃ ASTM D638 44 % bending strength Yield23℃ ASTM D790 93 Mpa Bending modulus 23℃ ASTM D790 2400 Mpa Impact strength of cantilever beam gap 23℃,-30℃ ASTM D256 55 J/m Impact strength of cantilever beam gap -30℃ ASTM D256 12 J/m Dart impact 55
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature Unannealed1.8MPa ASTM D648 80 °C Vicat softening temperature ASTM DI525 98 °C Vicat softening temperature 50℃/hr 50N ISO 306 98 °C Vicat softening temperature 120℃/hr 50N ISO 306 100 °C Vertical expansion coefficient ASTM D696 0.000080 cm/cm/℃
Physical properties شرایط آزمون روش آزمون نتیجه آزمون density ASTM D792 1.2 g/cm³ Shrinkage rate Flow3.2mm ASTM D995 0.5 % Shrinkage rate 垂直3.2mm ASTM D995 0.7 % Water absorption rate 23℃Saturation ISO 62 0.6 % Water absorption rate 23℃ 50RH ISO 62 0.2 % melt mass-flow rate 260℃ 2.16kg ASTM D1238 25 g/10min
flame retardant performance شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 2.50mm UL 94 V-0 UL flame retardant rating 3.00mm UL 94 V-0
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.