برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap 23°C, 3.20 mm, Injection ASTM D256 78 J/m
flammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 3.0 mm UL 94 V-0 UL flame retardant rating 1.5 mm UL 94 V-0
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون bending strength 23°C, 3.20 mm, Injection ASTM D790 137 Mpa Bending modulus 23°C, 3.20 mm, Injection ASTM D790 3920 Mpa tensile strength Yield, 23°C, 3.20 mm, Injection ASTM D638 83.4 Mpa
injection شرایط آزمون روش آزمون نتیجه آزمون Screw speed 40 to 70 rpm Back pressure 0.981 to 3.92 Mpa Mold temperature 90 to 120 °C Processing (melt) temperature 300 to 340 °C Spray nozzle temperature 290 to 330 °C Temperature at the front of the material cylinder 290 to 330 °C Temperature in the middle of the barrel 280 to 310 °C Temperature at the rear of the barrel 270 to 300 °C Suggested maximum moisture content 0.020 % drying time 3.0 to 5.0 hr drying temperature 100 to 200 °C
thermal performance شرایط آزمون روش آزمون نتیجه آزمون RTI UL 746 105 °C RTI Imp UL 746 90.0 °C RTI Elec UL 746 120 °C Hot deformation temperature 1.8 MPa, Unannealed, 6.40 mm, Injection ASTM D648 138 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate 23°C, 3.20 mm, Injection,Flow ASTM D955 0.20 - 0.40 % melt mass-flow rate 300°C/1.2 kg ASTM D1238 18 g/10 min density ASTM D792 1.25 g/cm³
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness R-Scale, 23°C, Injection ASTM D785 124