برگه داده فنی مقایسهother شرایط آزمون روش آزمون نتیجه آزمون remarks 通用
Basic Performance شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 200℃,5kg ASTM D-1238(ISO 1133) 5.5 g/10min melt mass-flow rate 200℃,10kg ASTM D-1238(ISO 1133) 35 g/10min Water absorption rate ASTM D-570 0.3 %
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Bending modulus ASTM D790/ISO 178 24000 kg/cm²(MPa)[Lb/in²] Rockwell hardness ASTM D785 110 tensile strength ASTM D638/ISO 527 480 kg/cm²(MPa)[Lb/in²] Elongation at Break ASTM D638/ISO 527 15 % Rockwell hardness ASTM D-785 110 R scale Impact strength of cantilever beam gap 6.4mm ASTM D-256 22 kg.cm/cm Bending modulus 23℃ ASTM D-790 24000 kg/cm bending strength 23℃ ASTM D-790 670 kg/cm elongation Break ASTM D-638 15 % tensile strength 23℃ ASTM D-638 480 kg/cm bending strength ASTM D790/ISO 178 670 kg/cm²(MPa)[Lb/in²]
thermal performance شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating UL -94 HB CLASS Hot deformation temperature 6.4mm,18.6kg/cm ASTM D-648 85 °C Combustibility (rate) UL 94 HB
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate ASTM D-75 0.4-0.7 % density ASTM D792/ISO 1183 1.04
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.