برگه داده فنی مقایسهoptical performance شرایط آزمون روش آزمون نتیجه آزمون Transmittance rate ASTM D1003/ISO 13468 91.0 %
other شرایط آزمون روش آزمون نتیجه آزمون Color 透明
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap ASTM D256/ISO 179 20 kg·cm/cm(J/M)ft·lb/in Elongation at Break ASTM D638/ISO 527 5.0 % tensile strength ASTM D638/ISO 527 70.3 kg/cm²(MPa)[Lb/in²] Rockwell hardness ASTM D785 95 bending strength ASTM D790/ISO 178 108 kg/cm²(MPa)[Lb/in²] Rockwell hardness M -Sale, 6.35 mm ASTM D785 95 tensile strength Yield, 3.18 mm ASTM D638 70.3 Mpa elongation Break, 3.18 mm ASTM D638 5.0 % bending strength 6.35 mm ASTM D790 108 Mpa Impact strength of cantilever beam gap 23℃, 6.35 mm ASTM D256 20 J/m
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature HDT ASTM D648/ISO 75 100 ℃(℉) Vicat softening temperature ASTM D1525/ISO R306 113 ℃(℉) Hot deformation temperature 1.8 MPa, Unannealed, 6.35 mm ASTM D648 100 °C Vicat softening temperature ASTM D1525 113 °C UL flame retardant rating 1.59 mm UL 94 HB
Physical properties شرایط آزمون روش آزمون نتیجه آزمون density ASTM D792/ISO 1183 1.16 melt mass-flow rate ASTM D1238/ISO 1133 1.8 g/10min melt mass-flow rate 230℃/3.8 kg ASTM D1238 1.8 g/10 min
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون transmissivity 3180 μm ASTM D1003 91.0 % turbidity 3.18 μm ASTM D1003 < 1.0 % Huangdu Index 3.18 mm ASTM D1003 0.50 to 1.0 YI