برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength Yield ASTM D-638 34 Mpa Bending modulus ASTM 790 1670 Mpa Impact strength of cantilever beam gap ASTM D-256 0.9 ft.lb/in Bending modulus ASTM D-790 17000 kg/cm Bending modulus ASTM D-790 240 psi bending strength ASTM D-790 39 Mpa tensile strength Yield ASTM D-638 350 kg/cm Impact strength of cantilever beam gap ASTM D-256 50 J/m elongation Break ASTM D-638 40 % tensile strength Yield ASTM D-638 5000 psi bending strength ASTM D-790 5700 psi Impact strength of cantilever beam gap ASTM D-256 5 kg.cm/cm bending strength ASTM D-790 400 kg/cm
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45Mpa ASTM D-648 130 °C Hot deformation temperature 1.82Mpa ASTM D-648 165 °F Hot deformation temperature 0.45Mpa ASTM D-648 265 °F Hot deformation temperature 1.82Mpa ASTM D-648 75 °C Burning rate ASTM D-UL94 HB
Physical properties شرایط آزمون روش آزمون نتیجه آزمون density ASTM D-792 0.98 Shrinkage rate ASTM D-955 1.3-1.6 %
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.