برگه داده فنی مقایسهoptical performance شرایط آزمون روش آزمون نتیجه آزمون gloss 45° ASTM D2457 32 turbidity ASTM D1003 20 %
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Vicat softening temperature ASTM D1525 104 °C Melting temperature Internal Method 123 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 190°C/2.16kg ASTM D1238 1.0 g/10min
film شرایط آزمون روش آزمون نتیجه آزمون tensile strength TD:Yield ASTM D882 10.5 Mpa tensile strength MD:Break ASTM D882 38.5 Mpa tensile strength TD:Break ASTM D882 36.3 Mpa elongation MD:Break ASTM D882 450 % elongation TD:Break ASTM D882 630 % Dart impact ASTM D1709B 1000 g Elmendorf tear strength MD ASTM D1922 280 g Elmendorf tear strength TD ASTM D1922 600 g film thickness 25 µm Thin film puncture strength Internal Method 6.67 J Thin film puncture strength Internal Method 68.9 N Thin film puncture strength Internal Method 32.3 J/cm³ Membrane strength MD ASTM D882 83.6 J/cm³ Membrane strength TD ASTM D882 95.1 J/cm³ Secant modulus 1%Secant,MD ASTM D882 218 Mpa Secant modulus 2%Secant,MD ASTM D882 188 Mpa Secant modulus 1%Secant,TD ASTM D882 251 Mpa Secant modulus 2%Secant,TD ASTM D882 209 Mpa tensile strength MD:Yield ASTM D882 10.4 Mpa
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.