برگه داده فنی مقایسهother شرایط آزمون روش آزمون نتیجه آزمون characteristic 性能特点:高透明度和冲击强度、高流动性、低厚度 purpose 家电部件.透明容器
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Charpy Notched Impact Strength ASTM D256/ISO 179 6 kg·cm/cm(J/M)ft·lb/in Elongation at Break ASTM D638/ISO 527 >500 % tensile strength ASTM D638/ISO 527 300 kg/cm²(MPa)[Lb/in²] Rockwell hardness ASTM D785 85 tensile strength Yield ASTM D638 300 kg/cm2 elongation Break ASTM D638 >500 % Impact strength of cantilever beam gap 23℃ ASTM D256 6.0 kg.cm/cm Bending modulus ASTM D790 1200 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature HDT ASTM D648/ISO 75 95 ℃(℉) Vicat softening temperature ASTM D1525/ISO R306 130 ℃(℉) Vicat softening temperature ASTM D1525 130 °C Hot deformation temperature HDT ASTM D648 95 °C turbidity ASTM D1003 6.0 % Heat accelerated aging 在150℃空气中 ASTM D3012 360 hr
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate ASTM D1238/ISO 1133 45 g/10min melt mass-flow rate ASTM D1238 45.0 g/min Rockwell hardness ASTM D785 85 R
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.