Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
42 kJ/m²
Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
55 kJ/m²
flammability
شرایط آزمون
روش آزمون
نتیجه آزمون
UL flame retardant rating
0.8mm
UL 94
HB
UL flame retardant rating
1.6mm
UL 94
HB
UL flame retardant rating
3.2mm
UL 94
HB
Burning wire flammability index
0.8mm
IEC 60695-2-12
650 °C
Burning wire flammability index
3.2mm
IEC 60695-2-12
650 °C
Extreme Oxygen Index
ISO 4589-2
24 %
flammability
FMVSS302
B30
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Tensile modulus
23°C
ISO 527-2
9800 Mpa
tensile strength
Yield,23°C
ISO 527-2
185 Mpa
Tensile strain
Break,23°C
ISO 527-2
2.5 %
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Hot deformation temperature
0.45MPa,Unannealed
ISO 75-2/B
260 °C
Hot deformation temperature
1.8MPa,Unannealed
ISO 75-2/A
250 °C
Continuous use temperature
IEC 60216
130 °C
Ball Pressure Test
125°C
IEC 60695-10-2
通过
Ball Pressure Test
165°C
IEC 60695-10-2
通过
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Shrinkage rate
TD:23°C
ISO 294-4
0.75 %
Shrinkage rate
MD:23°C
ISO 294-4
0.40 %
Water absorption rate
23°C,24hr
ISO 62
1.0 %
Water absorption rate
Saturation,23°C
ISO 62
5.5 %
Electrical performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Surface resistivity
IEC 60093
1E+13 ohms
Volume resistivity
23°C
IEC 60093
1E+15 ohms·cm
Dielectric strength
2.00mm
IEC 60243-1
21 KV/mm
Compared to the anti leakage trace index
3.20mm,SolutionA
IEC 60112
PLC 1