برگه داده فنی مقایسهother شرایط آزمون روش آزمون نتیجه آزمون characteristic 对金属有优异的耐摩擦和耐耗
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength ASTM D638 64 Mpa Elongation at Break ASTM D638 60 % bending strength ASTM D790 91 Mpa Bending modulus ASTM D790 2740 Mpa Impact strength of cantilever beam gap ASTM D256 78 J/m Rockwell hardness - ASTM D785 92 M Rockwell hardness - ASTM D785 120 R Wear resistance ASTM D1044 13 tensile strength ASTM D638/ISO 527 64 kg/cm²(MPa)[Lb/in²] elongation ASTM D638/ISO 527 60 % Rockwell hardness ASTM D785 92 Bending modulus ASTM D790/ISO 178 2740 kg/cm²(MPa)[Lb/in²] bending strength ASTM D790/ISO 178 91 kg/cm²(MPa)[Lb/in²]
thermal performance شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate ASTM D1238 9 g/10min Linear coefficient of thermal expansion TMA法 10 Hot deformation temperature 1.82MPa ASTM D648 125 °C Hot deformation temperature 0.45MPa ASTM D648 172 °C UL flame retardant rating UL 94 HB Combustibility (rate) UL 94 HB Hot deformation temperature HDT ASTM D648/ISO 75 125 ℃(℉) Linear coefficient of thermal expansion ASTM D696/ISO 11359 10 mm/mm.℃
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate Across Flow 旭化成法 1.8-2.2 % Water absorption rate ASTM D570 0.2 % Shrinkage rate Flow 旭化成法 1.8-2.2 % density ASTM D792/ISO 1183 1.42 melt mass-flow rate ASTM D1238/ISO 1133 9 g/10min melt mass-flow rate ASTM D1238/ISO 1133 0.2 g/10min
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.