برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Charpy Notched Impact Strength 0°C ISO 179/1eA 6.6 kJ/m² Charpy Notched Impact Strength 23°C ISO 179/1eA 10 kJ/m² Impact strength of cantilever beam gap 23°C ASTM D256A 150 J/m Charpy Notched Impact Strength -20°C ISO 179/1eA 4.8 kJ/m² Charpy Notched Impact Strength -30°C ISO 179/1eA 3.9 kJ/m² Gardner Impact -29°C,3.18mm ASTM D5420 22.7 J Impact strength of cantilever beam gap 23°C ISO 180/1A 8.4 kJ/m² Impact strength of cantilever beam gap -18°C ISO 180/1A 4.6 kJ/m² Impact strength of cantilever beam gap -40°C ISO 180/1A 4.0 kJ/m²
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون Bending modulus ISO 178 1250 Mpa Bending modulus --4,1%Secant ASTM D790B 1480 Mpa Bending modulus --3,1%Secant ASTM D790A 1290 Mpa Tensile strain Yield ISO 527-2/50 3.4 % elongation Yield ASTM D638 4.4 % tensile strength Yield ISO 527-2/50 24.3 Mpa tensile strength Yield ASTM D638 24.4 Mpa Tensile modulus ISO 527-2/1 1320 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 1.8MPa,Unannealed ISO 75-2/A 51.5 °C Hot deformation temperature 0.45MPa,Unannealed ISO 75-2/Bf 93.0 °C Hot deformation temperature 0.45MPa,Unannealed ASTM D648 105 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 230°C/2.16kg ASTM D1238 20 g/10min
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.