Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
Tensile modulus	23°C	ISO 527-2/1A	6200 Mpa
tensile strength	断裂, 23°C	ISO 527-2/1A	125 Mpa
Tensile strain	断裂, 23°C	ISO 527-2	3.0 %
Flexural modulus	23°C	ISO 178	5300 Mpa
bending strength	23°C	ISO 178	-- Mpa

Impact resistance	شرایط آزمون	روش آزمون	نتیجه آزمون
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	41 kJ/m²

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Surface Resistivity		IEC 60093	6.0E+15 ohms
Volume resistivity		IEC 60093	1.0E+15 ohms·cm
dielectric strength	2.00 mm	IEC 60243-1	31 KV/mm
Dissipation Factor		IEC 60250	0.010
Compared to the Leakage Tracking Index (CTI)	解决方案 A	IEC 60112	PLC 1

injection	شرایط آزمون	روش آزمون	نتیجه آزمون
drying temperature			80 °C
Suggested maximum moisture content			0.20 %
Temperature at the rear of the barrel			270 to 280 °C
Temperature in the middle of the barrel			275 to 285 °C
Temperature at the front of the material cylinder			280 to 290 °C
Temperature			70 to 100 °C

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	1.8 MPa, 未退火，HDT	ISO 75-2/Af	245 °C
melting temperature		ISO 11357-3	263 °C

نکات مهم: Plas.com داده‌های برگه فنی را از تولیدکنندگان مواد جمع‌آوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت داده‌ها انجام می‌دهد، اما هیچ مسئولیتی در قبال داده‌ها ندارد. اکیداً توصیه می‌شود که صحت داده‌ها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.