Instrumented dart impact energy 23 ℃ (73 ℉) total energy
/
ASTM D3763
63 J
Suspended wall beam without notch impact strength
/,23℃
ASTM D4812
3204 J/m
Impact strength of cantilever beam gap
23℃
ASTM D256
801 J/m
mechanical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
Rockwell hardness
ASTM D785
118
Bending modulus
1.3 mm/
ASTM D790
2340 Mpa
bending strength
1.3 mm/min/,Yield
ASTM D790
96 Mpa
Elongation at Break
Type I, 5
ASTM D638
130 %
elongation
Type I, 5,Yield
ASTM D638
7 %
tensile strength
Type I, 5,Break
ASTM D638
68 Mpa
tensile strength
Type I, 5,Yield
ASTM D638
62 Mpa
thermal properties
شرایط آزمون
روش آزمون
نتیجه آزمون
RTI Imp
UL 746B
130 °C
RTI Elec
UL 746B
130 °C
RTI Imp
UL 746B
130 °C
Vicat softening temperature
Rate B/50
ASTM D1525
154 °C
thermal performance
شرایط آزمون
روش آزمون
نتیجه آزمون
Combustibility (rate)
UL 94
HB
Physical properties
شرایط آزمون
روش آزمون
نتیجه آزمون
density
ASTM D792/ISO 1183
1.2
melt mass-flow rate
ASTM D1238/ISO 1133
10.5 g/10min
Bi Rong
/
ASTM D792
0.83
Water absorption rate
equilibriu
ASTM D570
0.35
Water absorption rate
equilibriu
ASTM D570
0.58
Water absorption rate
24 hours
ASTM D570
0.15
Shrinkage rate
flow, 3.2
Internal
0.5-0.7
melt mass-flow rate
/,300℃/1.2 kg
ASTM D1238
10.5 g/10min
hardness
شرایط آزمون
روش آزمون
نتیجه آزمون
Hardness (Rockwell R)
ASTM D 785
118 R
Hardness (Rockwell M)
ASTM D 785
70 M
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.