برگه داده فنی مقایسهflammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 2.0mm UL 94 5VB UL flame retardant rating 1.5mm UL 94 V-0
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون bending strength 23°C ISO 178 68.0 Mpa Bending modulus 23°C ISO 178 2500 Mpa tensile strength 23°C ISO 527-2 41.0 Mpa Tensile modulus 23°C ISO 527-2 2400 Mpa Impact strength of cantilever beam gap ASTM D256/ISO 179 13 kg·cm/cm(J/M)ft·lb/in bending strength ASTM D790/ISO 178 68 kg/cm²(MPa)[Lb/in²] Bending modulus ASTM D790/ISO 178 2500 kg/cm²(MPa)[Lb/in²] Rockwell hardness ASTM D785 103 tensile strength ASTM D638/ISO 527 41 kg/cm²(MPa)[Lb/in²] Tensile modulus ASTM D638/ISO 527 2400 kg/cm²(MPa)[Lb/in²] Impact strength of cantilever beam gap ASTM D256/ISO 179 5 kg·cm/cm(J/M)ft·lb/in
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Linear coefficient of thermal expansion MD ISO 11359-2 9E-05 cm/cm/°C Hot deformation temperature 1.8MPa,Unannealed ISO 75-2/Af 74.0 °C Linear coefficient of thermal expansion ASTM D696/ISO 11359 8 mm/mm.℃ Hot deformation temperature HDT ASTM D648/ISO 75 74 ℃(℉)
Physical properties شرایط آزمون روش آزمون نتیجه آزمون Shrinkage rate MD:23°C ISO 294-4 0.50-0.70 % Melt Volume Flow Rate (MVR) 220°C/10.0kg ISO 1133 30.0 cm3/10min melt mass-flow rate ASTM D1238/ISO 1133 30 g/10min Shrinkage rate ASTM D955 0.7-0.8 % density ASTM D792/ISO 1183 1.18
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness R-Sale,23°C ISO 2039-2 103