physical property	شرایط آزمون	روش آزمون	نتیجه آزمون
Shrinkage rate	MD2.0mm	ISO 294-4	0.75 %
Shrinkage rate	Shrinkage rate	TD2.0mm	ISO 294-4	0.75 %
Water absorption rate	(23°C,24hr)	ISO 62	1.00 %
Water absorption rate	Water absorption rate	(23°C,50RH)	ISO 62	0.20 %
melt mass-flow rate	260℃/5.0Kg	ISO 1133	15 cm3/10min

Mechanical properties	شرایط آزمون	روش آزمون	نتیجه آزمون
tensile strength	23°C	ISO 527-2	52 Mpa
elongation at break	23°C	ISO 527-2	>50 %
Tensile modulus	23°C	ISO 527-2	2200 Mpa
Impact strength of cantilever beam gap	23°C	ISO 180/1A	45 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	35 kJ/m²

Flame retardant performance	شرایط آزمون	روش آزمون	نتیجه آزمون
UL flame retardant rating		UL -94	HB 0.85mm
	UL flame retardant rating		UL -94	HB 1.50mm
	UL flame retardant rating	UL flame retardant rating		UL -94	HB 3.00mm

Electrical performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Volume resistivity		IEC 60093	1E+15 Ω.cm
Surface Resistivity		IEC 60093	1E+15 Ω.cm

Thermal performance	شرایط آزمون	روش آزمون	نتیجه آزمون
Heat distortion temperature	0.45MPa未退火，HDT	ISO 75-2/Bf	124 °C
Heat distortion temperature	Heat distortion temperature	1.80MPa退火，HDT	ISO 75-2/Af	103 °C
vicat		ISO 306/B50	119 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	8E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ISO 11359-2	8.5E-05 cm/cm/°C