برگه داده فنی مقایسهflammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating UL 94 HB
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength 23°C ASTM D638 62.0 Mpa elongation Break,23°C ASTM D638 40 % Bending modulus 23°C ASTM D790 2400 Mpa bending strength 23°C ASTM D790 84.0 Mpa tensile strength ASTM D638/ISO 527 630 kg/cm²(MPa)[Lb/in²] Bending modulus ASTM D790/ISO 178 24500 kg/cm²(MPa)[Lb/in²] bending strength ASTM D790/ISO 178 870 kg/cm²(MPa)[Lb/in²]
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45MPa,Unannealed ASTM D648A 158 °C Hot deformation temperature 1.8MPa,Unannealed ASTM D648A 110 °C Melting temperature ASTM D1525 166 °C Linear coefficient of thermal expansion MD ASTM D696 1.3E-04 cm/cm/°C Combustibility (rate) UL 94 HB Melting temperature 166 ℃(℉) Linear coefficient of thermal expansion ASTM D696/ISO 11359 13 mm/mm.℃
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 190°C/2.16kg ASTM D1238 11 g/10min Shrinkage rate MD ASTM D955 2.0 % Water absorption rate Equilibrium,23°C,60%RH ASTM D570 0.22 % density ASTM D792/ISO 1183 1.41 Shrinkage rate ASTM D955 2.0 %
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Surface resistivity ASTM D257 1E+13 ohms Volume resistivity ASTM D257 1E+11 ohms·cm Dielectric strength ASTM D149 19 KV/mm Dielectric constant ASTM D150 3.70 Dissipation factor 1MHz ASTM D150 0.060
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness M-Scale ASTM D785 80