برگه داده فنی مقایسهimpact performance شرایط آزمون روش آزمون نتیجه آزمون Impact strength of cantilever beam gap -30°C,3.20mm ASTM D256 69 J/m Impact strength of cantilever beam gap -30°C,6.40mm ASTM D256 69 J/m Impact strength of cantilever beam gap 23°C,3.20mm ASTM D256 250 J/m Impact strength of cantilever beam gap 23°C,6.40mm ASTM D256 210 J/m
flammability شرایط آزمون روش آزمون نتیجه آزمون UL flame retardant rating 1.0mm UL 94 HB UL flame retardant rating 2.5mm UL 94 V-0 UL flame retardant rating 2.0mm UL 94 V-0 UL flame retardant rating 1.5mm UL 94 V-0 UL flame retardant rating 3.0mm UL 94 V-0
mechanical properties شرایط آزمون روش آزمون نتیجه آزمون tensile strength Yield,3.20mm ASTM D638 44.1 Mpa Tensile modulus 3.20mm ASTM D638 2260 Mpa elongation Yield,3.20mm ASTM D638 5.0 % elongation Break,3.20mm ASTM D638 >20 % Bending modulus 6.40mm ASTM D790 2550 Mpa bending strength 6.40mm ASTM D790 68.6 Mpa
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Hot deformation temperature 0.45MPa,Unannealed,6.40mm ASTM D648 84.0 °C Hot deformation temperature 1.8MPa,Unannealed,6.40mm ASTM D648 76.0 °C Vicat softening temperature ASTM D15255 83.0 °C RTI Str UL 746 75.0 °C RTI Imp UL 746 75.0 °C RTI Elec UL 746 85.0 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون density ASTM D792 1.19 g/cm³ melt mass-flow rate 220°C/10.0kg ASTM D1238 60 g/10min Shrinkage rate MD:3.20mm ASTM D955 0.40-0.70 %
hardness شرایط آزمون روش آزمون نتیجه آزمون Rockwell hardness R-Scale ASTM D785 105
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.