برگه داده فنی
مقایسه
| physical property | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Shrinkage rate | 横向流量 | 内部方法 | 0.60 % |
| Shrinkage rate | 流量 | 内部方法 | 0.20 % |
| Water absorption rate | 饱和 | ASTM D570 | 0.020 % |
| hardness | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Rockwell hardness | R 级 | ASTM D785 | 106 |
| other | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| characteristic | | | 低翘曲性 耐磨性能良好 低粘度 流动性高 刚性高 耐化学性良好 |
| purpose | | | 电气 电子应用领域 连接器 线圈骨架 |
| flammability | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| UL flame retardant rating | 0.30 mm | UL 94 | V-0 |
| Limiting Oxygen Index | | ISO 527-1 | 40 % |
| Solder resistance | | 内部方法 | 300 °C |
| Mechanical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| elongation at break | | ASTM D638/ISO 527 | 5.1 % |
| Flexural modulus | | ASTM D790/ISO 178 | 11800 kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 158 kg/cm²(MPa)[Lb/in²] |
| tensile strength | | ASTM D638 | 157 Mpa |
| elongation | 断裂 | ASTM D638 | 5.1 % |
| Flexural modulus | 23°C | ASTM D790 | 11800 Mpa |
| bending strength | 23°C | ASTM D790 | 158 Mpa |
| Impact resistance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Suspended wall beam without notch impact strength | 6.40 mm | ASTM D256 | 250 J/m |
| Physical properties | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| density | | ASTM D792/ISO 1183 | 1.67 |
| Water absorption rate | | ASTM D570/ISO 62 | 0.020 % |
| Electrical performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Volume resistivity | | ASTM D257 | 1.0E+15 ohms·cm |
| dielectric constant | 1 MHz | ASTM D150 | 3.80 |
| dielectric constant | 1.00 GHz | ASTM D150 | 3.50 |
| Dissipation Factor | 1 MHz | ASTM D150 | 0.026 |
| Dissipation Factor | 1.00 GHz | ASTM D150 | 4.0E-3 |
| arc resistance | | ASTM D495 | 124 sec |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 3 |
| injection | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| drying temperature | | | 130 °C |
| drying time | | | 4.0 to 24 hr |
| Temperature at the rear of the barrel | | | 280 to 320 °C |
| Temperature in the middle of the barrel | | | 320 to 340 °C |
| Temperature at the front of the material cylinder | | | 340 to 360 °C |
| Spray nozzle temperature | | | 340 to 360 °C |
| Processing (melt) temperature | | | 350 °C |
| Temperature | | | 40 to 160 °C |
| Injection Pressure | | | 80.0 to 160 Mpa |
| injection speed | | | 中等偏快 |
| pressure holding | | | 20.0 to 40.0 Mpa |
| Back pressure | | | 1.00 to 5.00 Mpa |
| screw speed | | | 50 to 100 rpm |
| Thermal performance | شرایط آزمون | روش آزمون | نتیجه آزمون |
|---|
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 269 ℃（℉） |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ASTM D648 | 269 °C |
| Linear coefficient of thermal expansion | 流动 : 150°C | 内部方法 | 2.0E-6 cm/cm/°C |
| Linear coefficient of thermal expansion | 横向 : 150°C | 内部方法 | 8.5E-5 cm/cm/°C |