برگه داده فنی مقایسهmechanical properties شرایط آزمون روش آزمون نتیجه آزمون Elongation at Break ASTM D-638 20 % tensile strength ASTM D-638 480 kg/cm Rockwell hardness R-Scale ASTM D-785 105 Bending modulus ASTM D-790 24000 kg/cm impact elasticity Notched1/4" ASTM D-256 18 kgcm/cm Bending modulus ASTM D-790 750 kg/cm
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Vicat softening temperature 1.000g ASTM D-1525 97 °C Burning rate 1/16" UL -94 HB Hot deformation temperature Unannealed18.5kg/cm2,1/2" ASTM D-648 89 °C Burning rate 1/18" UL -94 HB
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 220℃/10kg ASTM D-1238 35 g/10min Shrinkage rate ASTM D-955 0.004-0.006 mm/mm
Electrical performance شرایط آزمون روش آزمون نتیجه آزمون Arc resistance ASTM D-495 PLC_6 Hot wire ignition UL -746A PLC 5 High voltage arc tracing rate UL -746A PLC 0 High arc combustion index UL -746A PLC 0 Compared to the anti leakage trace index UL -746A PLC 5 Burning rate 1/18" IEC 707 FH3-35 mm/min
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.