برگه داده فنی مقایسهoptical performance شرایط آزمون روش آزمون نتیجه آزمون turbidity 50.8μm ASTM D1003 1.1 % transparency 50.8μm ASTM D1746 83.0 gloss 20°,50.8μm ASTM D2457 141
thermal performance شرایط آزمون روش آزمون نتیجه آزمون Melting temperature Internal Method 99.0 °C Vicat softening temperature ASTM D1525 86.0 °C
Physical properties شرایط آزمون روش آزمون نتیجه آزمون melt mass-flow rate 190°C/2.16kg ASTM D1238 1.0 g/10min
film شرایط آزمون روش آزمون نتیجه آزمون tensile strength TD:Yield,51μm ASTM D882 6.89 Mpa tensile strength MD:Yield,51μm ASTM D882 7.24 Mpa Secant modulus 2%Secant,TD:51μm ASTM D882 92.4 Mpa Secant modulus 2%Secant,MD:51μm ASTM D882 91.7 Mpa Thin film puncture strength 51μm Internal Method 22.3 J/cm³ Thin film puncture strength 51μm Internal Method 92.5 N Thin film puncture strength 51μm Internal Method 8.81 J film thickness 51 µm Initial sealing temperature 51μm Internal Method 85.0 °C Elmendorf tear strength TD:51μm ASTM D1922 720 g Elmendorf tear strength MD:51μm ASTM D1922 550 g Dart impact 51μm ASTM D1709B >830 g elongation TD:Break,51μm ASTM D882 630 % elongation MD:Break,51μm ASTM D882 620 % tensile strength TD:Break,51μm ASTM D882 44.7 Mpa tensile strength MD:Break,51μm ASTM D882 58.6 Mpa
نکات مهم: Plas.com دادههای برگه فنی را از تولیدکنندگان مواد جمعآوری کرده است. Plas.com تمام تلاش خود را برای افزایش دقت دادهها انجام میدهد، اما هیچ مسئولیتی در قبال دادهها ندارد. اکیداً توصیه میشود که صحت دادهها را با تولیدکنندگان مواد تأیید کنید پیش از آنکه تصمیم نهایی بگیرید.